Eli-Crush FR866 Epoxy Crusher Backing Resin is a two part, ambient temperature curing, filler extended epoxy resin with good impact resistance and very low shrinkage.

The resin is mixed with aggregate particles and spread into place where it sets to a durable, flexible surface.

Eli-Crush FR866 shows no dermatitic properties and has a very low irritation potential at room temperature. It has low toxicity at ambient temperatures, however good industrial hygiene must be observed.

Typical applications include the lining of primary and secondary cone crushers, grinding mills, bonding, filling, fastening, grouting of holding bolts and mould making.

Kit size: 10kg
Easy to pour and mix
Minimal filler settlement in containers
Good penetration even at lower temperatures
Fast reactivity and outstanding mechanical properties
Good curing properties at lower temperatures

Specifications
Mix ratio	by volume: 100 parts resin to 11 part hardener by weight: 100 parts resin to 6 part hardener
Chemical resistance	resistant to solvents, aliphatic alcohols and aromatics
Curing time	2 hours at 20°C, 3 hours at 10°C
Coverage	please see chart in TDS below
Pot life	10-15 minutes at 25°C
Shelf life	12 months in sealed containers, must be stored in dry, cool conditions

Mixing

Block all cracks or gaps in the lining between the crusher and steel lining. If no adhesion is required, apply a grease or silicon based release agent to the crusher bowl before casting. Mix resin and hardener for 3 minutes using a spatula or other flat tool until a uniform colour is achieved.

Application

Pour immediately after mixing, working life is 10-15 minutes after mixing. Increases in temperature will shorten the working time, gel time and setting time. Decreases in temperature will extend the working time, gel time & setting time.